Characterization of deposit layers formed on grey cast iron

Monika Gwoździk

doi:10.31648/ts.7896

Characterization of deposit layers formed on grey cast iron

Monika Gwoździk

Politechnika Częstochowska

DOI: https://doi.org/10.31648/ts.7896

Abstrakt

This paper presents the results of diagnostic examinations conducted on the water pipe made of grey cast iron that were operated in conditions for 260 thousand hours. The tube was exposed in a soil. The phase composition of the deposit layers formed on both sides of the tube walls (outside and inside) was examined using optical and confocal microscopy and X-ray diffraction. The obtained XRD test results showed that mainly -FeOOH) and γ-FeOOH is formed on the inside of the pipe wall. In turn, on the outside, in addition to the above-mentioned compounds, also SiO₂ is formed. The results of these examinations have shown a higher degradation of pipe on the outer side. The arithmetic mean deviation of the profile from the mean line was 6.23 µm and 8.07 µm for the inner and outer side of the pipe wall, respectively. The work demonstrates the usefulness of material science, especially X-ray structure, topography and surface studies, in characterizing the degradation processes of layers formed on gray cast iron exploited in the water supply industry.

Słowa kluczowe:

water pipes, grey cast iron, deposits

Bibliografia

ASADI Z.S., MELCHERS R.E. 2018. Long-term external pitting and corrosion of buried cast iron water pipes. Corrosion Engineering Science Technology, 53: 93-101.
Crossref Google Scholar

CHEN W.X., CHEN J.R. 2022. Formation and prevention of pipe scale in water supply pipelines with anti-corrosion lining. Water Supply, 22: 4006-4014.
Crossref Google Scholar

GERKE T.L., SCHECKEL K.G., SCHOCK M.R. 2009. Identification and distribution of vanadinite (Pb5(V5+O4)3Cl in lead pipe corrosion by-products. Environmental Science & Technology, 43: 4412-4418.
Crossref Google Scholar

GUO H., CHEN H.L., ZHANG H.Y., LIU X.F., CHEN Y., TIAN Y.M., YIN J.H. 2020. Study on growth of corrosion scale on various iron based materials (grey cast iron/carbon steel/ductile iron) in water distribution systems. International Journal of Electrochemical Science, 15: 8479-8497.
Crossref Google Scholar

JONES L.J.N., KONG D., TAN B.T., RASSIAH P. 2021. Non-revenue water in malaysia: influence of water distribution pipe types. Sustainability, 13: 2310.
Crossref Google Scholar

LI M.J., LIU Z.W., CHEN Y.C. 2018. Physico-chemical characteristics of corrosion scales from different pipes in drinking water distribution systems. Water, 10: 931.
Crossref Google Scholar

MELCHERS R.E. 2017. Post-perforation external corrosion of cast iron pressurised water mains. Corrosion Engineering Science Technology, 52: 541-546.
Crossref Google Scholar

QI B.M., CUI C.W., YUAN Y.X. 2016. Effects of iron bacteria on cast iron pipe corrosion and water quality in water distribution systems. International Journal of Electrochemical Science, 11: 545-558. Google Scholar

RAJAKOVIC-OGNJANOVIC V.N., GRGUR B.N. 2011. Corroded scale analysis from water distribution pipes. Hemijska Industria, 65: 507-515.
Crossref Google Scholar

SHANKAR A.R., ANANDKUMAR B., THINAHARAN C., GEORGE R.P., ROOBY J., PHILIP J., MUDALI U.K. 2020. Corrosion evaluation of buried cast iron pipes exposed to fire water system for 30 years. Transactions of the Indian Institute of Metals, 73: 9-21.
Crossref Google Scholar

STEFAN E., RIPOSAN I., CHISAMERA M., STAN S. 2021. Lanthanum role in the graphite formation in gray cast irons. Minerals, 10: 1146.
Crossref Google Scholar

TIAN Y.M., YU T.T., SHEN J.Y., ZHENG G.L., LI H., ZHAO W.G. 2022. Cr release after Cr(III) and Cr(VI) enrichment from different layers of cast iron corrosion scales in drinking water distribution systems: the impact of pH, temperature, sulfate, and chloride. Environmental Science and Pollution Research, 29: 18778-18792.
Crossref Google Scholar

VERTOVA A., MIANI A., LESMA G., RONDININI S., MINGUZZI A., FALCIOLA L., ORTENZI M.A. 2019. Chlorine dioxide degradation issues on metal and plastic water pipes tested in parallel in a semi-closed system. International Journal of Environmental Research and Public Health, 16: 4582.
Crossref Google Scholar

WICHOWSKI P., KALENIK M., LAL A., MORAWSKI D., CHALECKI M. 2021. Hydraulic and technological investigations of a phenomenon responsible for increase of major head losses in exploited cast-iron water supply pipes. Water, 13: 1604.
Crossref Google Scholar

YANG F., SHI B.Y., GU J.N., WANG D.S., YANG M. 2012. Morphological and physicochemical characteristics of iron corrosion scales formed under different water source histories in a drinking water distribution system. Water Research, 46: 5423-5433.
Crossref Google Scholar

Pobierz